Tethon ceramic powder

Post by dragonator »

There has been quite a powder printing silence for the last few months. I have been busy, but not everything worked, and not everything was sharable.

On of the things that I now can share, is that I am working with 3D printed ceramics from Tethon. I got samples of stoneware, terra cotta, and porcelain, and their binder. I have not yet printed great amounts with it, but I do intend to do so.
IMG_20200716_193059s.jpg
IMG_20200716_193059s.jpg (381.03 KiB) Viewed 23219 times
IMG_20200716_193112s.jpg
IMG_20200716_193112s.jpg (465.91 KiB) Viewed 23219 times
Printing experience of this material in my inexperienced view. Great. It does pack a little, holding the part firm in the powder. It deposits new layers without disturbing previous layers. I have printed a test cylinder to test the dried properties. It is drying in the oven as I type. I have no idea what the white specks are, they do seem to be in the powder.
IMG_20200716_193130s.jpg
IMG_20200716_193130s.jpg (399.94 KiB) Viewed 23219 times
For cleaning more complex parts with powders that are actually fairly bad for you, I do have a proper negative pressure depowder chamber. Again, this is untested, but I hope it works fine. I is a foldable chamber (small gaps are hopefully no issue since the chamber is negative pressure) with a cyclonic separator on the back. I could have bought mine, but I wanted to try printing one. This version has 8 parallel cyclones. I do plan on adding an extra stage with even smaller cyclones on the back, but first I will see how this performs. If the front arm gaps leak too much powder I will add brushes. When the chamber works and there is interest I can share the plans for the woodwork and the cyclone.

All powder handling is done with respiratory equipment, since silicosis does not seem very desirable.
IMG_20200716_195106s.jpg
IMG_20200716_195106s.jpg (412.56 KiB) Viewed 23219 times
IMG_20200716_195121s.jpg
IMG_20200716_195121s.jpg (475.02 KiB) Viewed 23219 times
IMG_20200716_195130s.jpg
IMG_20200716_195130s.jpg (497.91 KiB) Viewed 23219 times
For the first few prints I will get a feel for the green and dry strengths, and how to handle this powder. I will then make prints that I will actually fire. I have a pottery workshop fairly close with a kiln that I can use.

More information will be shared when I have more progress.
maxt
Posts: 36
Joined: Fri Apr 26, 2019 10:38 am

Re: Tethon ceramic powder

Post by maxt »

Hi dragonator, which of the Tethon powders you are testing is the whitest one ?

and one more question, you said that the powder packs a little bit... do you know if it would clog the aspiration conducts of the zcorp printers ? Not sure if the printer you revitalized has a vacuum aspirator to test with...

The main problem with alternative powders for 3DS/Zcorp printers is not the print quality or the smoothness of the bed. It's that when you vacuum the print bed, it simply clogs the whole stuff and it takes hours to unclog :-(
User avatar
dragonator
Site Admin
Posts: 595
Joined: Fri Aug 14, 2015 4:48 pm
Location: The Nethelands
Contact:

Re: Tethon ceramic powder

Post by dragonator »

Hello,

Earthenware and porcelain are both roughly the same whiteness (unfired). I have yet to fire any parts.

None of my printers have integrated vacuums. Is that the aspiration conducts you are referring to? The feeding of the Tethon powder is fairly nice, though the surface does tend to be a bit rough. I still need to optimize the feed speeds to get that better.
User avatar
dragonator
Site Admin
Posts: 595
Joined: Fri Aug 14, 2015 4:48 pm
Location: The Nethelands
Contact:

Re: Tethon ceramic powder

Post by dragonator »

I have printed some more with Tethon. The ideal inkjet saturation seems to be 210%, or 1260DPI in the weeping direction (and 600 in the other) at a layer thickness of 0,1mm. I have printed a Moai, and a scaled espresso cup. Scaled so far, because I am not made of time. Once I know I can fire I will print full scale.

Printing is fairly nice, but I have run into an interesting issue. There is a weak spot every 12,7mm, or every sweep. The cup I printed separated on 2 very clean lines, the exact lines I was printing at. I have 2 options to fix this. The first is to force the motion so that it will be guaranteed to overlap. Make 12,7mm 12,65mm so I am absolutely certain that the layers of binder overlap. The other is to print the half overlapping inkjet pattern most printers make by default (viewtopic.php?p=6449#p6449).

I do first have a little vacation coming up, so I will not have time to implement this, but after I get back I will finally start with some software again. Hopefully I will also get to firing parts then.

IMG_20200802_165052-s.jpg
IMG_20200802_165052-s.jpg (441.36 KiB) Viewed 23069 times
maxt
Posts: 36
Joined: Fri Apr 26, 2019 10:38 am

Re: Tethon ceramic powder

Post by maxt »

dragonator wrote: Sat Aug 01, 2020 2:12 pm Hello,

Earthenware and porcelain are both roughly the same whiteness (unfired). I have yet to fire any parts.

None of my printers have integrated vacuums. Is that the aspiration conducts you are referring to? The feeding of the Tethon powder is fairly nice, though the surface does tend to be a bit rough. I still need to optimize the feed speeds to get that better.
Thanks.

yes, I mean the aspiration conducts. They clog very easily on the 3Ds Projets